High Heat Resistance

Outstanding Mechanical Performance

Low Moisture Absorption
PPS-CF Mechanical Properties
Property
PPS-CF
Tensile Strength
(X-Y direction)
170~180MPa
Tensile Strength
(X-Y direction)
100~110 MPa
Impact Strength
(X-Y direction)
25~30KJ/㎡
Modulus of Elasticity
(X-Y direction)
5500~6000 MPa
Elongation at Break
(X-Y direction)
1~3%
Melt Flow Rate
(MFR)
3~6 g/10min
Heat Deflection Temperature
(HDT@ 0.455 MPa/66 psi)
245℃
Density
1.3~1.31g/cm³
Water Absorption
(23°C/24h)
<0.1%
Specification
Drying Conditions before Printing
120°C, 5 hours (using a convection oven)
Nozzle Diameter
Ф0.4/0.6mm(Ф0.4mm recommended)
Layer Thickness
0.1~0.2mm
Nozzle Temperature
290~330°C
Build Plate Temperature
70~100°C
Printing Speed
40~150mm/s
(higher speeds require higher temperatures)
Cooling Fan
0~20%
Retraction Length
1~2m
Retraction Speed
20~40mm/s
Support Materials
Self-supporting, HIPS, PVA
Filament Diameter
1.75mm
Printing and Storage Environment Humidity
<20% RH (sealed with desiccant)