High Heat Resistance
High Rigidity
PPA-GF Mechanical Properties
Property
PPA-GF
Flexural Strength
(X-Y direction)
230~250 MPa
Tensile Strength
(X-Y direction)
210~230MPa
Impact Strength
(X-Y direction)
40~50KJ/㎡
Modulus of Elasticity
(X-Y direction)
4500~5000 MPa
Elongation at Break
(X-Y direction)
2~3%
Melt Flow Rate
(MFR)
3~6g/10min
Heat Deflection Temperature
(HDT@ 0.455 MPa/66 psi)
220℃
Density
1.32~1.35g/c㎡
Water Absorption
(23°C/24h)
<0.1%
Specification
Drying Conditions before Printing
100°C, 5 hours (using a convection oven)
Nozzle Diameter
Ф0.4/0.6mm(Ф0.4mm recommended)
Layer Thickness
0.12~0.3mm
Nozzle Temperature
260~290°C
Build Plate Temperature
70~100°C
Printing Speed
40~150mm/s
(higher speeds require higher temperatures)
Cooling Fan
0~20%
Retraction Length
1~2mm
Retraction Speed
20~40mm/s
Support Materials
Self-supporting
Filament Diameter
1.75mm
Printing and Storage Environment Humidity
Room temperature to 40'C, ≤20% RH (sealed with desiccant)