High elasticity
Chemical resistance
Wear resistance
High Thermal Stability
TPU 95A Mechanical Properties
Property
TPU 95A
Flexural Strength
(X-Y direction)
7~9 MPa
Tensile Strength
(X-Y direction)
27~28 MPa
Impact Strength
(X-Y direction)
NB
Elastic Modulus
(X-Y direction)
6~7 MPa
Elongation at Break
(X-Y direction)
800~1000%
Melting Flow Rate
(MFR)
6~10 g/10min
Heat Deflection Temperature
(HDT@ 0.455 MPa/66 psi)
95℃
Density
1.2~1.25 g/c㎡
Water Absorption
(23°C/24h)
<0.5%
Specification
Drying Conditions before Printing
70°C, 5 hours (using a convection oven)
Nozzle Diameter
Ф0.4/0.6mm(Ф0.4mm recommended)
Layer Height
0.12-0.3mm
Nozzle Temperature
180~240°C
Build Plate Temperature
25~60°C
Printing Speed
20~200mm/s
(higher speeds require higher temperatures)
Cooling Fan
50~100%
Retraction Length
0.3~1mm
Retraction Speed
30~50mm/s
Support Materials
Self-supporting, PVA, BVOH
Filament Diameter
1.75mm
Printing and Storage Environment Humidity
Room temperature to 40'C, ≤20% RH (sealed with desiccant)