Easy to Print
Dimensional Stability
Matte effect
Low grain
High stiffness
Eco-friendly and Biodegradable
PLA Matte Mechanical Properties
Property
PLA Matte
Flexural Strength
(X-Y direction)
63~65 MPa
Tensile Strength
(X-Y direction)
50~55 MPa
Impact Strength
(X-Y direction)
7~9 KJ/㎡
Elastic Modulus
(X-Y direction)
1500~1700 MPa
Elongation at Break
(X-Y direction)
6~7%
Melting Flow Rate
(MFR)
4~8 g/10min
Heat Deflection Temperature
(HDT@ 0.455 MPa/66 psi)
53℃
Density
1.23~1.25 g/c㎡
Water Absorption
(23°C/24h)
<0.5%
Specification
Drying Conditions before Printing
50°C, 5 hours (using a convection oven)
Nozzle Diameter
Ф0.4/0.6mm(Ф0.4mm recommended)
Layer Thickness
0.18~0.3mm
Nozzle Temperature
190~240°C
Build Plate Temperature
25~60°C
Printing Speed
40~300mm/s
(higher speeds require higher temperatures)
Cooling Fan
50~100%
Retraction Length
1~2mm
Retraction Speed
30~50mm/s
Support Materials
Self-supporting, PVA, BVOH
Filament Diameter
1.75mm/2.85mm
Printing and Storage Environment Humidity
Room temperature to 40'C, ≤20% RH (sealed with desiccant)