PLA Galaxy Mechanical Properties
Property
PLA Luminous
Flexural Strength
(X-Y direction)
69~75MPa
Tensile Strength
(X-Y direction)
45~49 MPa
Impact Strength
(X-Y direction)
4.5~5 KJ/㎡
Modulus of Elasticity
(X-Y direction)
1000~1100 MPa
Elongation at Break
(X-Y direction)
13.5~15.5%
Heat Deflection Temperature
(HDT@ 0.455MPa/66psi)
4-8g/10min
Melt Flow Rate
(MFR)
53℃
Water Absorption
(23°C/24h)
1.25~1.26 g/cm³
Density
<0.3%
Specification
Drying Conditions before Printing
50°C, 5hours (using a convection oven)
Nozzle Diameter
Ф0.4/0.6mm(Ф0.4mm recommended)
Layer Height
0.12~0.3mm
Nozzle Temperature
190~240°C
Build Plate Temperature
25~60°C
Printing Speed
40~250mm/s
(higher speeds require higher temperatures)
Cooling Fan
50~100%
Retraction Length
1~2mm
Retraction Speed
30~50mm/s
Support Materials
Self-supporting, PVA, BVOH
Filament Diameter
1.75mm
Printing and Storage Environment Humidity
Room temperature to 40'C, ≤20% RH (sealed with desiccant)