PETG-A opaque Mechanical Properties
Property
PETG-A Opaque
Flexural Strength
(X-Y direction)
50~55 MPa
Tensile Strength
(X-Y direction)
40~45 MPa
Impact Strength
(X-Y direction)
4.5~5 KJ/㎡
Modulus of Elasticity
(X-Y direction)
1000~1100 MPa
Elongation at Break
(X-Y direction)
6~8%
Melting Flow Rate
(MFR)
4~6g/10min
Heat Deflection Temperature
(HDT@ 0.455 MPa/66 psi)
74℃
Density
1.27~1.28 g/c㎡
Water Absorption
(23°C/24h)
<0.2%
Specification
Pre-printing Drying Conditions
70°C, 5 hours (using a convection oven)
Nozzle Diameter
Ф0.4mm
Layer Thickness
0.12~0.3mm
Nozzle Temperature
230~250°C
Build Plate Temperature
70~80°C
Printing Speed
40~60mm/s
(higher speeds require higher temperatures)
Cooling Fan
0~50%
Retraction Length
1~2mm
Retraction Speed
30~50mm/s
Support Materials
Self-supporting
Filament Diameter
1.75mm
Printing and Storage Environment Humidity
Room temperature to 40°C, ≤20% RH (sealed with desiccant)