Property

PET-CF

Flexural Strength

(X-Y direction)

140~150MPa

Tensile Strength
(X-Y direction)

75~85 MPa

Impact Strength
(X-Y direction)

25~30KJ/㎡

Modulus of Elasticity
(X-Y direction)

4500~5000 MPa

Elongation at Break
(X-Y direction)

4~5%

Melt Flow Rate
(MFR)

3~6 g/10min

Heat Deflection Temperature
(HDT@ 0.455 MPa/66 psi)

205℃

Density

1.3~1.31g/cm³

Water Absorption
(23°C/24h)

0.3%

Drying Conditions before Printing
100°C, 5 hours (using a convection oven)

Nozzle Diameter
Ф0.4/0.6mm(Ф0.4mm recommended)

Layer Thickness
0.12~0.3mm

Nozzle Temperature
260~290°C

Build Plate Temperature
70~100°C

Printing Speed

40~150mm/s
(higher speeds require higher temperatures)

Cooling Fan
0~20%

Retraction Length
4~6mm

Retraction Speed
20~40mm/s

Support Materials
Self-supporting, HIPS

Filament Diameter
1.75mm

Printing and Storage Environment Humidity
Room temperature to 40'C, ≤20% RH (sealed with desiccant)