Continuous Use up to 160°C
Low Shrinkage
Maintains 50% Mechanical Properties at High Temperatures
Excellent Strength and Impact Resistance
Low Moisture Absorption
High Heat Resistance
PAHT Mechanical Properties
Property
PAHT
Flexural Strength
(X-Y direction)
75~80 MPa
Tensile Strength
(X-Y direction)
66.5~68 MPa
Impact Strength
(X-Y direction)
5.5-6 KJ/㎡
Elastic Modulus
(X-Y direction)
2400~2500 MPa
Elongation at Break
(X-Y direction)
12.5~14%
Melting Flow Rate
(MFR)
5~7 g/10min
Heat Deflection Temperature
(HDT@ 0.455 MPa/66 psi)
90℃
Density
1.14~1.15 g/c㎡
Water Absorption
(23°C/24h)
0.5%
Specification
Drying Conditions before Printing
80°C, 12h (using a convection oven)
Nozzle Diameter
Ф0.4/0.6mm(Ф0.4mm recommended)
Layer Thickness
0.12~0.3mm
Nozzle Temperature
260~280°C
Build Plate Temperature
80~110°C
Printing Speed
40~120mm/s
(higher speeds require higher temperatures)
Cooling Fan
20~50%
Retraction Length
3~5mm
Retraction Speed
30~50mm/s
Support Materials
Self-supporting, PVA, BVOH
Filament Diameter
1.75 mm
Printing and Storage Environment Humidity
Room temperature to 40'C, ≤20% RH (sealed with desiccant)