High Strength
High Wear Resistance
High strength and high rigidity
PA6-GF Mechanical Properties
Property
PA6-GF
Flexural Strength
(X-Y direction)
100~130 MPa
Tensile Strength
(X-Y direction)
75~85 MPa
Impact Strength
(X-Y direction)
50~60 KJ/㎡
Elastic Modulus
(X-Y direction)
3000~3500 MPa
Elongation at Break
(X-Y direction)
2~4%
Melting Flow Rate
(MFR)
3~6 g/10min
Heat Deflection Temperature
(HDT@ 0.455 MPa/66 psi)
200℃
Density
1.32~1.35 g/c㎡
Water Absorption
(23°C/24h)
1%
Specification
Drying Conditions before Printing
100°C,5h (convection oven)
Nozzle Diameter
Ф0.4/0.6mm(Ф0.4mm recommended)
Layer Thickness
0.12~0.3mm
Nozzle Temperature
250~270°C
Build Plate Temperature
80~110°C
Printing Speed
40~150mm/s
(higher speeds require higher temperatures)
Cooling Fan
0~20%
Retraction Length
1~2mm
Retraction Speed
20~40m/s
Support Materials
Self-supporting, HIPS
Filament Diameter
1.75mm
Printing and Storage Environment Humidity
Room temperature to 40'C, ≤20% RH (sealed with desiccant)