Property

PA1010

Flexural Strength
(X-Y direction)

72.5~76.5 MPa

Tensile Strength
(X-Y direction)

38~40 MPa

Impact Strength
(X-Y direction)

3.5~6.5 KJ/㎡

Elastic Modulus
(X-Y direction)

1200~1300 MPa

Elongation at Break
(X-Y direction)

8~10%

Melting Flow Rate
(MFR)

2~5 g/10min

Heat Deflection Temperature
(HDT@ 0.455 MPa/66 psi)

90℃

Density

1.01~1.02 g/c㎡

Water Absorption
(23°C/24h)

0.30%

Drying Conditions before Printing
80°C, 8h (using a convection oven)

Nozzle Diameter
Ф0.4/0.6mm(Ф0.4mm recommended)

Layer Thickness

0.12~0.3mm

Nozzle Temperature
220~260°C

Build Plate Temperature
60~100°C

Printing Speed

40~200mm/s
(higher speeds require higher temperatures)

Cooling Fan
20~50%

Retraction Length
3~5mm

Retraction Speed
30~50mm/s

Support Materials
Self-supporting, PVA, BVOH

Filament Diameter
1.75mm

Printing and Storage Environment Humidity
Room temperature to 40'C, ≤20% RH (sealed with desiccant)