Property

PETG

HS PETG

Flexural Strength
(X-Y direction)

50~55 MPa

64~66 MPa

Tensile Strength
(X-Y direction)

40~45 MPa

41~45 MPa

Impact Strength
(X-Y direction)

4.5~5 KJ/㎡

5~6 KJ/㎡

Elastic Modulus
(X-Y direction)

1000~1100 MPa

1400~1500 MPa

Elongation at Break
(X-Y direction)

6~8%

10~12%

Melting Flow Rate
(MFR)

4~6 g/10min

8~12 g/10min

Heat Deflection Temperature
(HDT@ 0.455 MPa/66 psi)

74℃

68℃

Density

1.27~1.28 g/c㎡

1.27~1.28 g/c㎡

Water Absorption
(23°C/24h)

<0.2%

<0.2%

Drying Conditions before Printing
70°C, 5 hours (Convection Oven)

Nozzle Diameter
Ф0.4/0.6mm(Ф0.4mm recommended)

Layer Height
0.12~0.3mm

Nozzle Temperature
220~270°C

Build Plate Temperature
Room temperature to 60°C

Printing Speed

100~350mm/s
(higher speeds require higher temperatures)

Cooling Fan
50~100%

Retraction Length
1~2mm

Retraction Speed
30~50mm/s

Support Materials
Self-supporting, PVA, BVOH

Filament Diameter
1.75/2.85mm

Printing and Storage Environment Humidity
Room temperature to 40'C, ≤20% RH (sealed with desiccant)