High Flowability
Fast Printing
Easy to Print
Dimensional Stability
High Rigidity
HS PETG Mechanical Properties
Property
PETG
HS PETG
Flexural Strength
(X-Y direction)
50~55 MPa
64~66 MPa
Tensile Strength
(X-Y direction)
40~45 MPa
41~45 MPa
Impact Strength
(X-Y direction)
4.5~5 KJ/㎡
5~6 KJ/㎡
Elastic Modulus
(X-Y direction)
1000~1100 MPa
1400~1500 MPa
Elongation at Break
(X-Y direction)
6~8%
10~12%
Melting Flow Rate
(MFR)
4~6 g/10min
8~12 g/10min
Heat Deflection Temperature
(HDT@ 0.455 MPa/66 psi)
74℃
68℃
Density
1.27~1.28 g/c㎡
1.27~1.28 g/c㎡
Water Absorption
(23°C/24h)
<0.2%
<0.2%
Specification
Drying Conditions before Printing
70°C, 5 hours (Convection Oven)
Nozzle Diameter
Ф0.4/0.6mm(Ф0.4mm recommended)
Layer Height
0.12~0.3mm
Nozzle Temperature
220~270°C
Build Plate Temperature
Room temperature to 60°C
Printing Speed
100~350mm/s
(higher speeds require higher temperatures)
Cooling Fan
50~100%
Retraction Length
1~2mm
Retraction Speed
30~50mm/s
Support Materials
Self-supporting, PVA, BVOH
Filament Diameter
1.75/2.85mm
Printing and Storage Environment Humidity
Room temperature to 40'C, ≤20% RH (sealed with desiccant)