Property

PLA Silk Dual Color

Flexural Strength
(X-Y direction)

72~75 MPa

Tensile Strength
(X-Y direction)

45~49 MPa

Impact Strength
(X-Y direction)

5~6 KJ/㎡

Elastic Modulus
(X-Y direction)

1150~1250 MPa

Elongation at Break
(X-Y direction)

10.5~12.5%

Melting Flow Rate
(MFR)

5-10 g/10min

Heat Deflection Temperature
(HDT@ 0.455 MPa/66 psi)

53℃

Density

1.25~1.26 g/c㎡

Water Absorption
(23°C/24h)

＜0.3%

Drying Conditions before Printing
55°C, 8 hours (using a convection oven)

Nozzle Diameter
Ф0.4/0.6mm(Ф0.4mm recommended)

Layer Thickness

0.12~0.3mm

Nozzle Temperature
190~240°C

Build Plate Temperature
25~60°C

Printing Speed

40~300mm/s
(higher speeds require higher temperatures)

Cooling Fan
50~100%

Retraction Length
1~2mm

Retraction Speed
30~50mm/s

Support Materials
Self-supporting, PVA, BVOH

Filament Diameter
1.75mm/2.85mm

Printing and Storage Environment Humidity
Room temperature to 40'C, ≤20% RH (sealed with desiccant)