High Strength
High Toughness
Low Warpage
Excellent Layer Adhesion
High Heat Resistance
BPA-Free Composition
PC Mechanical Properties
Property
PC
Flexural Strength
(X-Y direction)
83~87 MPa
Tensile Strength
(X-Y direction)
40~45 MPa
Impact Strength
(X-Y direction)
4~5.5 KJ/㎡
Elastic Modulus
(X-Y direction)
1800~1950 MPa
Elongation at Break
(X-Y direction)
7~9%
Melting Flow Rate
(MFR)
3~5 g/10min
Heat Deflection Temperature
(HDT@ 0.455 MPa/66 psi)
123℃
Density
1.2~1.21 g/c㎡
Water Absorption
(23°C/24h)
<0.8%
Specification
Drying Conditions before Printing
80°C, 8h (using a convection oven)
Nozzle Diameter
Ф0.4/0.6mm(Ф0.4mm recommended)
Layer Thickness
0.12~0.3mm
Nozzle Temperature
240~270°C
Build Plate Temperature
100~120°C
Printing Speed
40~250mm/s
(higher speeds require higher temperatures)
Cooling Fan
0~50%
Retraction Length
0.3~2mm
Retraction Speed
30~50mm/s
Support Materials
Self-supporting, HIPS, PVA
Filament Diameter
1.75mm
Printing and Storage Environment Humidity
Room temperature to 40'C, ≤20% RH (sealed with desiccant)